Appraisal of composite's polymerization
Abstract
Light curing composites are widely used in therapeutic dentistry when teeth are restored. But there are some complications that are connected with features of composite's polymerization. During this work it was made comparative analysis of polymerization's depth of different composite materials using halogen, diode and polyvalent polymerization apparatus with and without heating.
References
1. Даронч М., Руеггеберг Ф., Де Гоуз М. Конверсия мономеров в предварительно нагретом композите // ДентАрт. -2007. - № 1. - С. 55-61.
2. Кондит М., Лейнфелдер К. Улучшение полимеризации композитов // ДентАрт. - 2007. - № 2. - С. 31-34.
3. Пат. 2280418. Российская Федерация. МПК A61C5/00 (2006. 01) A61C5/04 (2006. 01) Способ пломбирования зубов с полостями I-II классов [Текст]. Адамчик А.А., Адамчик Ал.А., Арутюнов А.В. Заявитель и патентообладатель Адамчик А.А. (RU), Адамчик Ал.А. (RU), Арутюнов А.В. (RU). - № 2005101112/14; заявл. 19. 01. 2005; опубл. 27.07.2006, бюл. № 21. - 5 с.
4. Blalock J.S., Holmes R., Rueggeberg F.A. Effect of temperature on unpolymerized composite resin film thickness // J. prosthet. dent. - 2006. - Vol. 96. № 424. - P. 32.
5. Daronch M., Rueggeberg F.A., Hall G., De Goes M.F. Effect of composite temperature on in vitro intrapulpal temperaturerise // Dent. mater. - 2007. - Vol. 23. № 1283. - P. 8.
6. Daronch M., Rueggeberg F.A., De Goes M.F., Guidici R. Polymerization kinetics of Pre-heated composite // J. dent. res. - 2006. - Vol. 85. № 38. - P. 43.
7. Floyd C.J.E., Dickens S.H. Network structure of BisGMA- and UDMA-based resin systems // Dent. mater. - 2006. -Vol. 22. № 1143. - P. 1149.
8. Opdam N.J., Roeters J.J., Joosten M., Veeke O. Porosities and voids in dass I restorations placed by six opera tors using a packable or syringable composite // Dent. mater. - Vol. 18. - P. 58-63.
9. Pfeifer C.S., Shelton Z.R., Braga R.R., Windmoller D., Machado J.C., Stansbury J.W. Characterization of dimethacrylate polymeric networks: a study of the crosslinked structure formed by monomers used in dental composites // European polymer journal. - 2010. - Vol. 2. № 47. - P. 162-170.
10. Rueggeberg F.A., Daronch M., De Goes M.F. Monomer conversion of pre-heated composite // J. dent. res. - 2005. -№ 84 (7). - P. 663-667.
11. Uctasli M.B., Arisu H.D., Lasilla L.V., Valittu P.K. Effect of preheating on the mechanical properties of resin composites // Eur. j. dent. - 2008. - Vol. 2. № 263. - P. 8.
12. Viljanen E.K., Skrifvars M., Vallittu P.K. Dendritic copolymers and particulate filler composites for dental applications: degree of conversion and thermal properties // Dent. mater. - 2007. - Vol. 23. № 1420. - P. 1427.
13. Walter R., Swift E., Heikh H., Ferracane J.L. Effects of temperature on composite resin shrinkage // Quintessence int. - 2009. - Vol. 40. № 843. - P. 7.
14. Wagner W.C., Asku M.N., Neme A.L., Linger J.B., Pink F.E., Walker S. Effect of pre-heating resin composite on restotation microleakage // Oper. dent. - 2008. - Vol. 33. № 72. - P. 8.
Review
For citations:
Adamchik A.A. Appraisal of composite's polymerization. Kuban Scientific Medical Bulletin. 2015;(1):7-11. (In Russ.)
Views:
299
Email this article 